Spectroscopic properties

of fluorophosphate glass

with high Er3+ concentration

ABSTRACT Fluorophosphate glass with 4 mol.% ErF3 content

was prepared. The different scanning calorimetry was

conducted. Raman spectrum, infrared transmission spectrum,

absorption spectrum were measured. Fluorescence spectrum

and lifetime of emission around 1.53 μm were measured under

970 nm laser diode excitation. The metaphosphate content in

the composition is limited, but the maximum phonon energy of

glass amounts to 1290 cm−1, and is comparatively high. The

full width at half maximum is about 56 nm, and is wider than

for most of the materials investigated. The measured lifetime of

4I13/2 → 4I15/2 transition, contributed by the high phonon energy,

inefficient interaction of Er3+ ions, and low water content,

amounts to no less than 7.36 ms though the Er3+ concentration

is high. This work might provide useful information for the

development of compact optical devices.

1 Introduction

In recent years researchers have paid a great deal

of attention tominiature rare earth-doped glass devices. Compact

devices such as microchip lasers, amplifiers, lossless

splitters, and waveguide lasers have already been demonstrated

[1–5]. Among them erbium-doped glass waveguides

have been of particular interest because of their potential for

use as active elements in integrated optical devices for optical

communication system.

Miniature devices, which are only a few centimeters in

length, require the glass to provide a gain per unit length

as large as possible. The gain per unit length is linear proportional

to NEr ×τ ×σemi, where NEr is the concentration

of Er3+ ions, τ is the fluorescence lifetime of Er3+: 4I13/2 →

4I15/2 transition and σemi is the stimulated-emission cross section,

so in order to obtain high gain per unit length, the concentration

of Er3+ ions should be as high as possible. However,

the concentration is limited by the concentration quenching.

Generally the concentration of Er3+ ions for the onset of concentration

quenching is no more than 1–2×1020 ions/cm3

for tellurite glasses or phosphate glasses [6, 7]. Above the

concentration, the lifetime decreases sharply with the increase

of Er3+ concentration. The fluorescence lifetime of

Er3+: 4I13/2 → 4I15/2 transition is a critical factor not only

because it contributes to high gain properties, but also because

a long lifetime permits the required high population

inversion to be obtained under steady-state conditions by exertion

of modest pump power [8]. In this paper, a glass with

considerably high Er3+ concentration as well as long fluorescence

lifetime was obtained. The Er3+ concentration is

7.45×1020 ions/cm3, and the measured lifetime amounts to

no less than 7.36 ms.

Характеристики

Тип файла документ

Документы такого типа открываются такими программами, как Microsoft Office Word на компьютерах Windows, Apple Pages на компьютерах Mac, Open Office - бесплатная альтернатива на различных платформах, в том числе Linux. Наиболее простым и современным решением будут Google документы, так как открываются онлайн без скачивания прямо в браузере на любой платформе. Существуют российские качественные аналоги, например от Яндекса.

Будьте внимательны на мобильных устройствах, так как там используются упрощённый функционал даже в официальном приложении от Microsoft, поэтому для просмотра скачивайте PDF-версию. А если нужно редактировать файл, то используйте оригинальный файл.

Файлы такого типа обычно разбиты на страницы, а текст может быть форматированным (жирный, курсив, выбор шрифта, таблицы и т.п.), а также в него можно добавлять изображения. Формат идеально подходит для рефератов, докладов и РПЗ курсовых проектов, которые необходимо распечатать. Кстати перед печатью также сохраняйте файл в PDF, так как принтер может начудить со шрифтами.

Список файлов статьи