Mech. Prop. (739416), страница 3
Текст из файла (страница 3)
Platinum (Thermocouple Quality, Annealed)
Tensile Strength, Ultimate 143 MPa
Gold
Hardness, Vickers 25
Tensile Strength, Ultimate 120 MPa Annealed
Elongation at Break 30%
Modulus of Elasticity 77,2 GPa 60% Cold Worked
Poisson's Ratio 0,42
Shear Modulus 32 GPa 60% Cold Worked; Calculated Value
Thallium
Hardness, Brinell 2
Hardness, Vickers 2
Tensile Strength, Ultimate 7,5 MPa
Elongation at Break 40% in 125 mm
Lead
Hardness, Brinell 4,2 Cast
Hardness, Vickers 5
Tensile Strength, Ultimate 18 MPa
Modulus of Elasticity 14 GPa
Poisson's Ratio 0,42
Bismuth
Hardness, Brinell 7
Modulus of Elasticity 31,7 GPa
Poisson's Ratio 0,33
Shear Modulus 14 GPa Calculated
Thorium
Hardness, Vickers 35–114 References report a wide range of values
Tensile Strength, Ultimate 200 MPa
Tensile Strength, Yield 144 MPa 0,2% offset
Elongation at Break 34%
Modulus of Elasticity 73,1 GPa
Compressive Yield Strength 200 MPa Approximately equal to tensile
Bulk Modulus 57,7 GPa
Poisson's Ratio 0,27
Fatigue Strength 97 MPa reversed bend test endurance limit
Shear Modulus 28 GPa
Protactinium
Bulk Modulus 157 GPa
Uranium (Cast)
Hardness, Brinell 185 Converted from Vickers for 3000 kg load/10 mm ball Brinell test Unspecified heat treatment
Hardness, Rockwell A 55 Unspecified heat treatment
Hardness, Rockwell B 90 Unspecified heat treatment
Hardness, Rockwell C 10 Unspecified heat treatment
Hardness, Vickers 190 Unspecified heat treatment
Tensile Strength, Ultimate 400 MPa
Tensile Strength, Yield 200 MPa
Elongation at Break 4%
Modulus of Elasticity 190 GPa
Poisson's Ratio 0,22
Shear Modulus 86 GPa Calculated
Uranium (Beta-Annealed)
Tensile Strength, Ultimate 615 MPa
Uranium (Wrought Α Phase)
Tensile Strength, Ultimate 1150 MPa
Tensile Strength, Yield 740 MPa
Elongation at Break 14%
Neptunium
Hardness, Vickers 346
Bulk Modulus 118 GPa
Shear Modulus 80 GPa
Plutonium
Hardness, Brinell 242 Converted from Vickers for 3000 kg load/10 mm ball Brinell test
Hardness, Rockwell A 62
Hardness, Rockwell C 22
Hardness, Vickers 250
Tensile Strength, Ultimate 400 MPa Cast α
Tensile Strength, Yield 275 MPa Cast α
Elongation at Break 0,2–0,5% Cast α
Modulus of Elasticity 96,5 GPa Cast
Compressive Yield Strength 415 MPa
Ultimate Compressive Strength 830 MPa
Poisson's Ratio 0,15–0,21
Fatigue Strength 90 MPa 100,000,000 cycles, rotating beam
Shear Modulus 45 GPa
Americium
Bulk Modulus 45 GPa
Curium
Bulk Modulus 37 GPa
Berkelium
Bulk Modulus 52 GPa
Californium
Bulk Modulus 50 GPa
Einsteinium
Bulk Modulus 15 GPa Estimated
Fermium
Bulk Modulus 15 GPa Estimated
Mineral Hardness (by Mohs) from
Г. В. Самсонов. Справочник "Свойства элементов".В 2 т. Москва, 1976 г.
| Symbol | Mohs HM |
| Li | 0,6 |
| Be | 5,5 |
| B | 9,3 |
| Diamond (С) | 10 |
| Na | 0,5 |
| Mg | 2,5 |
| Al | 2,75 |
| Si | 6,5 |
| S | 2 |
| K | 0,4 |
| Ca | 1,75 |
| Ti | 6 |
| V | 7 |
| Cr | 8,5 |
| Symbol | Mohs HM |
| Mn | 6 |
| Fe | 4 |
| Co | 5 |
| Ni | 4 |
| Cu | 3 |
| Zn | 2,5 |
| Ga | 1,5 |
| Ge | 6 |
| As | 3,5 |
| Se | 2 |
| Rb | 0,3 |
| Sr | 1,5 |
| Zr | 5 |
| Nb | 6 |
| Mo | 5,5 |
| Ru | 6,5 |
| Rh | 6 |
| Pd | 4,75 |
| Ag | 2,5 |
| Cd | 2 |
| In | 1,2 |
| Sn | 1,5 |
| Sb | 3 |
| Te | 2,25 |
| Cs | 0,2 |
| Ba | 1,25 |
| La | 2,5 |
| Ce | 2,5 |
| Hf | 5,5 |
| Ta | 6,5 |
| W | 7,5 |
| Re | 7 |
| Os | 7 |
| Ir | 6,5 |
| Pt | 3,5 |
| Au | 2,5 |
| Tl | 1,2 |
| Pb | 1,5 |
| Bi | 2,25 |
| Th | 3 |
| U | 6 |
7